Materials » Single Sided » Masking Tapes Fine Line and Flatback

Product Tape Structure (Backing/Anhesive) Total Thickness mils (mm) Adhesion oz./in. (N/100mm) Tensile Strength lbs./in. width (N/100mm) Elongation at Break % Temperature Range °F(°C) Comments
Fine Line Masking Tapes
215 Blue, Plastic Film/Rubber 4.7 (0.12) 48 (53) 10 (175) 460 Up to 250°F ( 121°C ) Up to 40 min. Medium temperature.
218 Green Matte Finish, Polypropylene Film/Rubber 4.8 (0.12) 39 (43) 13 (228) 490 Up to 250°F ( 121°C ) Up to 30 min. Medium temperature.
222 White Polyester Film/Acrylic 2.4 (0.06) 24 (26) 26 (455) 127 Up to 325°F ( 163°C ) Up to 1 hour High temperature.
4735 Orange Vinyl Film/Rubber 5.5 (0.14) 15 (16) 15 (260) 130 Up to 300°F ( 149°C ) Up to 30 min. High temperature.
4737S Opaque Blue Vinyl Film/Rubber 5.1 (0.13) 14 (15) 14 (245) 150 Up to 325°F ( 163°C ) Up to 1 hour High temperature.
4737T Translucent Blue Vinyl Film/Rubber 5.1 (0.13) 14 (15) 17 (297) 150 Up to 325°F ( 163°C ) Up to 1 hour High temperature.
Flatback Tapes
250 Tan Flat Stock Paper/Rubber 5.9 (0.15) 65 (71) 62 (1086) 3 Up to 250°F ( 121°C ) Up to 30 min. PPP-T- 42C , Type II
256 Red/White/Green Flat Stock Paper/Rubber 6.7 (0.17) 30 (33) 25 (438) 5 Up to 200°F ( 93°C ) Up to 1 hour Printable, accepts marking inks.
2515 Tan Flat Stock Paper/Rubber 6.7 (0.17) 55 (60) 36 (630) 3 Up to 200°F ( 93°C ) Up to 30 min. General purpose splicing, . holding and bundling applications.
2517 Tan Flat Stock Paper/Rubber 6.4 (0.16) 74 (80) 36 (630) 4 Up to 300°F ( 149°C ) Up to 1 hour Excellent splicing, holding and bundling applications.
2525 Orange Flat Stock Paper/Rubber 9.5 (0.24) 69 (75) 49 (858) 2 Up to 300°F ( 149°C ) Up to 1 hour Premium splicing, holding and bundling applications.
2526 White Flat Stock Paper/Rubber 9.8 (0.242) 69 (75) 50 (858) 4 Up to 300°F ( 149°C ) Up to 1 hour Excellent adhesion and strength for textile applications.
Note: This technical information and data should be considered representative or typical only and should not be used for specification purposes.